TYPICAL PROPERTIES OF CURED MATERIAL
Physical Properties
Coefficient of Thermal Expansion, :
Below Tg, ppm/°C 33
Glass Transition Temperature (Tg) by TMA, °C 240
Bulk Thermal Conductivity, W/(m-K):
@ 90°C 1.1
@ 165°C 1.0
Tensile Modulus, DMTA :
Cured 30 minutes @ 300oC N/mm2 10,000
(psi) (1,450,377)
Extractable Ionic Content, @ 100°C:
Chloride (Cl-) <10
Sodium (Na+) <15
Potassium (K+) <15
Decomposition (in N2):
TGA analysis @ 10oC/ minute ramp from 25 to 400
oC
@ 340oC, % 0.2
@ 400oC, % 0.3
Electrical Properties
Sample cured 30 minutes @ 300oC
Volume Resistivity, ohm-cm ≤0.01
TYPICAL PERFORMANCE OF CURED MATERIAL
Die Shear Strength:
2 X 2 mm Si die, kg-f,
cured 20 minutes @ 150oC
Substrate DSS
Ag/Cu LF ≥5
Tensile Strength :
cured 30 minutes @ 300oC, MPa
After Cure After 1000 TC'C"
>17 >17
Radius of Curvature:
Si die on Alumina, meters
cured 30 minutes @ 300oC
Chip Size: ROC
15 x 15 mm > 5
BLETHERM 2600AT高導(dǎo)熱導(dǎo)電銀膠 黏 度： 8.5 PaS 剪切強度： - Mpa 工作時間： 1440 min 工作溫度： - ℃ 保 質(zhì) 期： 12 個月 固化條件： 30分鐘升到200°C + 15分鐘 @ 200°C 主要應(yīng)用： 大功率LED
HENKEL ABLETHERM 2600AT粘合劑是一款特別為芯片需要高散而開發(fā)的芯片粘接膠,如大功率和和散熱元氣件. 本粘合劑是一種特的懸浮液-銀和樹脂顆粒懸浮在溶劑載體中. 一旦膠水完全固化,溶劑也會干掉, 本粘合劑含有很高比重的銀. 本品主要用于高功率,高導(dǎo)熱的大功率發(fā)光二極管.
漢高樂泰導(dǎo)電膠,楊浦厚膜漢高ABLESTIKJM7000導(dǎo)電膠
面議
產(chǎn)品名：漢高ABLESTIKJM7000導(dǎo)電膠,JM7000導(dǎo)電膠,漢高導(dǎo)電膠,樂泰導(dǎo)電膠
ablestik84-1A導(dǎo)電膠
面議
產(chǎn)品名：導(dǎo)電膠,耐高溫導(dǎo)電膠,84-1A導(dǎo)電膠,84-1LMI導(dǎo)電膠
遼陽樂泰454瞬干膠快干膠
面議
產(chǎn)品名：樂泰454 瞬干膠,快干膠
鹽城樂泰SI5910密封膠硅基密封膠
面議
產(chǎn)品名：樂泰SI 5910 密封膠,硅基密封膠
克拉瑪依樂泰M18養(yǎng)護劑
面議
產(chǎn)品名：樂泰M18養(yǎng)護劑,金屬養(yǎng)護劑
彰化縣樂泰EA3463環(huán)氧修補劑環(huán)氧修補劑
面議
產(chǎn)品名：樂泰EA 3463環(huán)氧修補劑,環(huán)氧修補劑
河源樂泰SI5970密封膠
面議
產(chǎn)品名：樂泰 SI5970 密封膠,硅酮密封劑
彭水樂泰5910密封膠法蘭密封膠
面議
產(chǎn)品名：樂泰5910 密封膠,法蘭密封膠